16 Carbon nanotubes are one of the strongest materials known to engineers. They have an elastic modulus of 1.1 TPa (1TPa = 10¹2 Pa). If a carbon nanotube has a diameter of 15 nm determine the engineering stress, in GPa, sustained by the nanotube when subjected to a tensile load of 4 µN along the length of the tube. Assume that the entire cross-sectional area of the nanotube is load bearing. 3.14. Enter the answer rounded to one place after the decimal (xx.x). Do not enter the units. Note: This answer will be required in the next question so please note this down. Type your answer... 17 Carbon nanotubes are one of the strongest materials known to engineers. They have an elastic modulus of 1.1 TPa (1TPa = 10¹2 Pa). Assume that the carbon nanotube is only deformed elastically under a load of 4 uN. The carbon nanotube has a length of 10 pm. what is the elongation of carbon nanotube in nanometres. Use the engineering s om previous Q16. Enter the rounded integer answer without decimal place. Do not enter the units. Type your answer...

16 Carbon nanotubes are one of the strongest materials known to engineers. They have an elastic modulus of 1.1 TPa (1TPa = 10¹2 Pa). If a carbon nanotube has a diameter of 15 nm determine the engineering stress, in GPa, sustained by the nanotube when subjected to a tensile load of 4 µN along the length of the tube. Assume that the entire cross-sectional area of the nanotube is load bearing. 3.14. Enter the answer rounded to one place after the decimal (xx.x). Do not enter the units. Note: This answer will be required in the next question so please note this down. Type your answer... 17 Carbon nanotubes are one of the strongest materials known to engineers. They have an elastic modulus of 1.1 TPa (1TPa = 10¹2 Pa). Assume that the carbon nanotube is only deformed elastically under a load of 4 uN. The carbon nanotube has a length of 10 pm. what is the elongation of carbon nanotube in nanometres. Use the engineering s om previous Q16. Enter the rounded integer answer without decimal place. Do not enter the units. Type your answer...

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A steel column is a cylinder 6.8 m long and 0.35 m in diameter. What is the change in length of the column when it experiences a tensile stress resulting from the application of a 3600 N force? The elastic modulus for steel is 20 × 1010 Nm2/kg2. ΔL = m
A copper cylinder with a length of 1.5 m and diameter of 4 cm undergoes compression. Bulk Modulus (14*10^10 Pa) What will be the bulk strain of the copper rod if pressure is applied to reduce its volume to 0.00089 m3? How much pressure was applied to the copper rod? Calculate the percent change in volume of the copper rod.
A tube has 25mm outside diameter and an axial tensile load of 40 kN. If the strain on the tube is limited to 0.1% and density of 7800kg/m^3, what is the maximum internal diameter of the tube in mm?
A tensile force of 200 KN is applied on a 0.02-m diameter and.2-m long rod. After applying the load, the diameter of the rod decreases to 0.01998 m and the length increases to 2.01 m. Assuming no permanent deformation occurs in that material, the modulus of elasticity (GPa) is?
A titanium tube with an outside diameter of 25 mm and inside diameter of 20 mm and a length of 200 mm. When an elastic uniaxial tensile force of 30 kN is applied to this tube along its length, what is the final length of that tube? (Modulus of elasticity of Titanium is 105 GPa)
A steel [E = 200 GPa] rod with a circular cross section is 9-m long. Determine the minimum diameter D required if the rod must transmit a tensile force of 21 kN without stretching more than 4 mm.
A long metal plate (E = 210 GPa) with some cutouts in it is mounted between two rigid plates at 6 am. By noon, the temperature has risen by 20°C. The structure is made from aluminium with a coefficient of thermal expansion of a = 23 x 10-6/°C. Please use the stress concentration chart shown below for any relevant calculations. a10 h L b O Use the following values in your working out: K 3.2 3.0 2.8 2.6 2.4 2.2 2.0 L = 13 m 0 0.1 P 0.2 W W Javg 0.3 2r P (w2r)t 0.4 P ▬▬▬▬▬▬▬ 0.5 h = 5.3 m a = 0.8 m b = 1.6 m a) What is the average normal stress throughout the plate at noon? b) What is the maximum stress at any point in the structure? c) The material the plate is made from has a tensile yield stress of 416 MPa and a compressive yield stress of 200 MPa. Using these values, do you expect the plate to yield at/before noon?
A cylindrical structural element is made of steel. The element must withstand an axial load of 160 kN. Determine the diameter of its cross section so that it does not have plastic deformation. What is the load that this element resists if it is 80 cm long and suffers an elongation of 200 micrometers? Consider an elastic modulus of 200 G Pa. And a yield stress of 340 M Pa. Use a factor of safety of 3/5 with respect to the yield stress.
Stress (MPa) 500 400 Consider the brass alloy for which the stress-strain behavior is shown in the Animated Figure 7.12. A cylindrical specimen of this material 9.9mm (0.3898 in.) in diameter and 98.8mm (3.890 in.) long is pulled in tension with a force of 9780N(2199/b). If it is known that this alloy has a value for Poisson's ratio of 0.35, compute (a) the specimen elongation, (b) the reduction in specimen diameter. Note: because the diameter decreases, enter a minus sign in your answer. Tensile strength 450 MPa (65,000 psi), Strain =0 Stress = 0 MPA Stress =0 psi 70 Strain = 0 Stress 0 MPA 60 Stress = 0 psi 103 psi 50 40 MPa Yield strength 300 250 MPa (36,000 psi) 40 30 200 200 20 100 10 100 0 0 T 10 P 0.10 0.20 Strain 10.065 0 0.30 0.40 30 20 10 Stress (10 psi)
A band of polyisoprene is to hold together a bundle of steel rods for up to 1 year (52 weeks). If the stress on the band is less than 10MPa at that stage, the band will not hold the rods tightly any longer. Determine the initial stress that must be applied to the polyisoprene band when it is slipped over the steel. A series of tests showed that an initial stress of 7MPa decreased to 6.8MPa after 6 weeks. A. None of the mentioned/ Geen van die genoemde B. σ = 13.03 MPa C. σ = 10.29 MPa D. σ = 11.73 MPa
A thin plate is subjected to a biaxial stress field of  x= 1 Gpa and  y= 0.5 Gpa. Calculate the strains in the xy directions if the plate is made of (a) steel, (b) a 0° unidirectional boron-epoxy composite. For the boron-epoxy composite use the following properties: Young’s Modulus at 0°=207 Gpa, modulus at 90° = 19 Gpa,  12=0.21, G12= 6.4 Gpa. Assume for steel a young’s modulus = 207 GPa
How does the slenderness ratio affect the buckling behavior of columns in mechanical engineering?