A cylindrical specimen of steel having an original diameter of 12.8 mm (0.505 in.) is tensile tested to fracture and found to have an engineering fracture strength o, of 460 MPa (67,000 psi). If its cross-sectional diameter at fracture is 10.7 mm (0.422 in.), determine: (a) The ductility in terms of percent reduction in area. (b) The true stress at fracture.

A cylindrical specimen of steel having an original diameter of 12.8 mm (0.505 in.) is tensile tested to fracture and found to have an engineering fracture strength o, of 460 MPa (67,000 psi). If its cross-sectional diameter at fracture is 10.7 mm (0.422 in.), determine: (a) The ductility in terms of percent reduction in area. (b) The true stress at fracture.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A cylindrical specimen of mild steel having 20% ductility (in percentage of reduction in area) is tensile tested and fractured at a stress of 600 MPa. If original diameter is 10 mm, what is the true stress at fracture. O 810 MPa 492MPA O 602 MPa O 750 MPa
In tensile test a plain carbon steel specimen has a (40mm) gauge length and the Final area (A final) of specimen after tensile test was 264.327. The load which caused fracture was (122.5 KN). After fracture, the final length was 47.516mm True stress at fracture is. * O 463.441 N/mm2, O 525.441 N/mm2, O 254.441 N/mm2, 498.441 N/mm2,
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: i) Initial Length (in mm) = ii) Final Area (in mm2) = iii) Initial Area (in mm2) =
A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the true fracture stress if the final diameter of the specimen at the location of the fracture was 0.350 in. Stress (ksi) 120 Upper scale Lower scale H 0.0 0.020 0.040 0.060 0.080 0.100 0.120 0.0 0.002 0.004 0.006 0.008 0.010 0.012 Strain (in./in.) 90 60 30 0- 300 ksi O 126 ksi EA O 237 ksi O 202 ksi O 261 ksi
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
Problem: A tensile test specimen of stainless steel alloy having a with a diameter of 12.6 mm and a 50 mm gage length was tested to fracture. Load and deformation data obtained during the test are given: Determine: (a) the modulus of elasticity. (b) the proportional limit. Load (kN) 0.00 Change in length (mm) (c) the ultimate strength. 0.00 (d) the yield strength (0.20% offset). 0.00 25.79 0.00 (e) the fracture stress. 0.05 51.59 0.10 (f) the true fracture stress if the final diameter 66.55 73.36 80.18 87.77 0.20 of the specimen at the location of the fracture 0.30 0.45 was 8.89 mm 0.63 95.35 0.81 101.42 105.98 112.05 1.01 1,18 1.41 only solve d, e,f 118.13 123.46 128.03 131.85 133.39 134.95 135.73 1.66 1.94 2.27 2.60 2,82 3.15 3.35 3.68 136.53 136.56 3.93 135.84 4.26 135.14 4,66 133.66 4.94 130.67 5.22 5.47 128.44 124.69 5.70 120.92 5.82 117.91 5.95 fracture 116.52
1 Q 4 N Current Attempt in Progress 30¹ F1 A specimen of a 4340 steel alloy with a plane strain fracture toughness of 54.8 MPa m (50 ksi vin.) is exposed to a stress of 978.0 MPa (141800 psi). Assume that the parameter Y has a value of 1.18. - Your answer is partially correct. @ 2 (a) If the largest surface crack is 0.9 mm (0.03543 in.) long, determine the critical stress o. i 1608.13 (b) Will this specimen experience fracture? W S Yes v eTextbook and Media Hint Save for Later 38 command F2 # 3 E D 80 F3 X C $ 4 R MPa 000 000 F4 F % 5 V F5 T G 6 B MacBook Pro Y H & 44 N U 8 J Attempts: 1 of 5 used en l M 9 K DD F9 0 < H I -O L Submit Answer A F10 P V . t C F11 { command option [ + " = ? |
A tensile test specimen of 1045 hot-rolled steel having a diameter of 0.505 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the ultimate strength. Stress (ksi) 60 50- 40- 30- 20 10- 0 0 0 Upper scale O 66 ksi 28 ksi O 72 ksi O 53 ksi O 62 ksi Lower scale. 0.025 0.050 0.075 0.100 0.125 0.150 0.175 0.002 0.004 0.006 0.008 0.010 0.012 0.014 Strain (in./in.)
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 60 % - Percentage of Reduction in Area = 36 % - Final length after fracture = 35.2 mm - Final Diameter after fracture = 3.54 mm & - Ultimate stress = 439 MPa iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
A brass specimen of the circular cross-section is fractured at 159 kN force and the final length of the specimen at fracture is 51 mm. The fracture strength of the specimen is found to be 85 kN/mm2. The percentage of elongation of the specimen is 42 %. Determine the following 4-Stress under an elastic load of 14 kN 5-Young's Modulus if the elongation is 1.5 mm at 14 kN 6-Final diameter if the percentage of reduction in area is 27 %.
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 44 % - Final length after fracture = 36.3 mm - Final Diameter after fracture = 4.39 mm & - Ultimate stress = 359 MPa Determine the Initial length, Initial diameter and Maximum load. SOLUTION: i) Initial Length (in mm) = ii) Final Area (in mm2) = iii) Initial Area (in mm2) = iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
A tensile test specimen of stainless steel alloy having a diameter of 0.495 in. and a gage length of 2.00 in. was tested to fracture. Stress and strain data obtained during the test are shown. Determine the proportional limit. Stress (ksi) 40 30- 20 10- 0- 0.0 0.0 Upper scale 0.020 0.002 22 ksi O 15 ksi E 19 ksi O 10 ksi 13 ksi Lower scale- 0.040 0.060 0.080 0.100 0.004 0.006 0.008 0.010 Strain (in./in.) 0.120 0.012