ase calculate the strain and stress in the following two prompts a. A 1 cm long section of tendon stretches to 1.011 cm when it is subjected to a tensile force of 40,000 N. What is the strain in this segment of tendon? 1.011 cm A% E = Δι Lo O = F - = b. The section of the patellar ligament in the previous question is 0.02 m² in the cross section. What is the stress in this section of ligament as a result of 50,000 N tensile force? 16,000 A = 30000 0.02 = = strain 2500000 N/m²

ase calculate the strain and stress in the following two prompts a. A 1 cm long section of tendon stretches to 1.011 cm when it is subjected to a tensile force of 40,000 N. What is the strain in this segment of tendon? 1.011 cm A% E = Δι Lo O = F - = b. The section of the patellar ligament in the previous question is 0.02 m² in the cross section. What is the stress in this section of ligament as a result of 50,000 N tensile force? 16,000 A = 30000 0.02 = = strain 2500000 N/m²

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The strain rosette shown in figure was used to obtain strain data at a point on the surface of a machine part. If the readings from gages a, b, c were 650, -450, -585 (all in microns) respectively; which of the following is the shear strain on the surface? 45° a Lutfen birini seçin a1370 micron b. 1570 micron c1400 micron d7600 micron
1-A round member having a diameter of 3cm experience an axial load of 10KN. Two strain gauges are mounted on the member, one measuring an axial strain of 600 micro-strain and the other measuring a lateral strain of -163 micro-strain. The modulus of elasticity in GPa is Choose... The Poisson ratio is Choose... + The stress in MPa is Choose... + Next page
QB3 TWO DIMENTIONAL STRAINThree strain gauges were arranged in the form of a rectangular rosette and positioned on atest surface. The measured strains were as follows: 1 = 200x 10-6 2 = 100 x 10-6 3 = 50 x 10-6Determinea) the principal strains and the principle stressesb) the direction of the greater principal strain relative to gauge 1 and sketch the Mohrstrain circle. Take the Young Modulus of Elasticity value to be E = 200 GN/m2 andPoisson’s ratio  = 0.28.
Semiconductor strain gauges find their primary application in the construction of transducers, such as load cells and pressure transducers. Why do measuring instruments manufacturers usually use semiconductor strain gauges even though they are significantly more expensive than metallic strain gauges? Name two pros and two cons of these strain gauges compared to metallic strain gauges. Paragraph B A Lato (Recom... 19px... v T + v
material with a rectangular cross-section of 4 mm by 25 mm is loaded in tension with a force of 32 kN. A strain gauge bonded to the material measures a strain of 400 microstrain when the sample is loaded. culate Young's modulus of the material, measured to the nearest GPa (GN/m2) and enter your answer in the box below. ung's modulus: [ GPa
You need the shear modulus for a particular material in order to calculate shear strain for a known applied shear shear stress. You can't find shear modulus for the material, but you can find elastic modulus (200 GPa) and Poisson's ratio (0.3). Which of the following could you use as the shear modulus for your calculations? 200 GPa O 60 GPa O 77 GPa O 154 GPa
X Slide 1 Final exam (Remately Procto x lockdown Question 1.16 The state of stress at a point is represented by Point A on the Mohr's circle shown in Figure Q1.16. The angle of inclination with respect to Point A corresponding to the minimum normal stress is B 6S 140° A Figure Q1.16 Hido T O a. 40° O b. -20° O c. 140° O d. 50° 11 Proctorio is sharing your screen. Ston sharing
6. State your answers to the following questions.Strain Gauge represents the deformation of a material through a change in resistance. If so, explain how temperature will affect the strain gauge in the experimental environment.①:In this experiment, the Strain Gauge measures the strain in micro units. Explain one possible error factor when applying a load by hanging a weight on the material with the strain gauge attached. (Hint: It is easy to shake by hanging the weight using a thread)①:
A single strain gauge is mounted to measure the axial strain in a simple tensile member the recorded strain is 200 microstrain, what is the axial stress ? a) If the member is of steel? b) if the member is of aluminium ? The modulus of elasticity of steel is 200 GN/m² and that of aluminium is 70 GN/m²
The strain components, ex= 940 micro strain, ey= -360 micro strain and yxy=830micro strain are given for a point in body subjected to plane strain. Determine; a. Magnitude of the principal strains b. The direction of the principal strain axes c. The maximum in-plane shear strain. Confirm your answer by means of Mohr's circle of strain and determine the linear strain on an axis inclined at 20 degrees clockwise to the direction of ey
The following data was obtained as a result of tensile testing of a standard 0.505 inch diameter test specimen of magnesium. After fracture, the gage length is 2.245 inch and the diameter is 0.466 inch. a). Calculate the engineering stress and strain values to fill in the blank boxes and plot the data. Load(lb) Gage Length (in) Stress (kpsi) Strain 0 2 1000 2.00154 2000 2.00308 3000 2.00462 4000 2.00615 5000 2.00769 5500 2.014 6000 2.05 6200 (max) 2.13 6000 (fracture) 2.255 b). Calculate the modulus of elasticity c). If another identical sample of the same material is pulled only to 6000 pounds and is unloaded from there, determine the gage length of the sample after unloading.
b) A 1.25 m long cable has a diameter 3.50 mm with a Young's Modulus, E, of 9.75 x 10⁹ N/m². When the wire is placed under tension, it experiences a stress of 202.52 x 106 N/m², the length of the cable extends by 36.35 mm. Calculate the force that the cable experiences under tension and the strain energy density (U/V) due to deformation. Give your answers in newtons (N) to 2 decimal places for the force; and in joules per cubic metre (J/m³) for the strain energy density to 2 decimal places. Assume the cable is solid and the material is homogeneous. c) Figure Q1c shows a bracket on rollers that allow the bracket to move along a beam in the horizontal direction. A force F₁ of 2625 N acts at point A where the angle between F, and the x-axis is 100. If force F₂ acts at an angle a = 400 between F2 and the y-axis: (i) Determine the magnitude of F2 necessary to maintain bracket on horizontal equilibrium. (ii) Determine the vertical force at A acting along the y-axis. Give your answers to the…