Composition (at% C) 10 15 20 25 1600 1538°C 1493°C L. 1400 2500 1394°C y+L 1200 1147°C 2.14 4.30 Y. Austenite 2000 1000 912°C Y+ Fegc 800 1500 727°C 0.76 0.022 600 a, Ferrite a+ Fezc Cementite (Fe3C) 1000 400 6.70 (Fe) Composition (wt% C) Figure 2: Iron- carbon phase diagram (a) State THREE (3) solubility categories of the phase diagram. (b) By referring to the Iron-Carbon phase diagram in Figure 2: (1) Determine the maximum solubility of carbon in a iron (ferrite) and in y-iron (austenite). (ii) Calculate the percentage of phases (a and y) present at 728°C for 0.5%wt carbon. Temperature ("C) Temperature ("F)

Composition (at% C) 10 15 20 25 1600 1538°C 1493°C L. 1400 2500 1394°C y+L 1200 1147°C 2.14 4.30 Y. Austenite 2000 1000 912°C Y+ Fegc 800 1500 727°C 0.76 0.022 600 a, Ferrite a+ Fezc Cementite (Fe3C) 1000 400 6.70 (Fe) Composition (wt% C) Figure 2: Iron- carbon phase diagram (a) State THREE (3) solubility categories of the phase diagram. (b) By referring to the Iron-Carbon phase diagram in Figure 2: (1) Determine the maximum solubility of carbon in a iron (ferrite) and in y-iron (austenite). (ii) Calculate the percentage of phases (a and y) present at 728°C for 0.5%wt carbon. Temperature ("C) Temperature ("F)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

A 200g hypoeutectoid plain carbon steel contains 5.1wt% eutectoid ferrite. 1) What is its average carbon content in weight? 2) What is the weight of total ferrite? 1600 8+7 Liquid 1400 L+ Fe;C L+y 1200 1148°C y austenite 1000 2.0 4.3 y + Fe,C 800 e 723°C 600 0.8 0.02 400 a + Fe,C Fe;C 200 0% C 100% Fe 6 6.67 Fe,C 3 4 Weight percent carbon Temperature ("C)
For a Fe-C alloy with a eutectoid composition, an austenite was rapidly cooled down to 450°C, held for 10 sec, and quenched to room temperature. What is the final microstructure based on its TTT curve? Amount Temperature of Transformation, C 700 600 500 400 300 200 Ae₂! Ae₁ Austenite unstable Ms. 10 10² 103 104 105 seconds Austenite stable 50%- 100 MF TELEP P 100% completed F+B Coarse Pearlite - Fine Pearlite -Upper Bainite (Feathery) Lower Bainite → Martensite + Bainite Martensite 1 1sec 1 min 1hr Transformation Time (Log. Scale) O a. 50% bainite and 50% martensite O b. 50% austenite and 50% bainite O c. 100% bainite O d. 100% martensite Finer Lamellac Bainitic Pearlitic Austenite Fine more Acicular Rapid Etching Martensitic cicular, Slow Etching V.P.H. 210 320 450 700 750
1. four processes. 2. Fill out the blanks by labeling the phase regions. 3. Identify the Indicate an in- termediate compound, if any. 3. Temperature (°C) 1600 1400 1200 1000 800 600 400 1538°C 0 (Fe) -1493°C 1394°C 912°C y, Austenite 1 2 0.16 5 0,022 a, Ferrite A N 2.14 Composition (at% C) 15 10 3 1147°C L4 3 4 Composition (wt% C) 4.30 727°C Sketch the microstructure at A, label phases, figure out compositions. 20 Cementite (Fe3C). 5 6 25 6.70
16) What is the Eutectiod Composition/Point in this system?
1 4 7 8. 9. 10 QUESTION 1 For a 1% steel, the carbon is completely soluble in iron at: 1600 C 1400°C liquid 910°C Y + cementite Fe,C cementite| 723°C a + cementite 0% weight % carbon 7% 723°C 1000 °C 1400 °C None of above QUESTION 2 Which is the eutectic reaction? Click Save and Submit to save and submit. Click Save All Answers to save all answers.
Excellent combinations of hardness, strength, and toughness are obtained from bainite. One heat treater austenitized a eutectoid steel at 750°C, quenched and held the steel at 250°C for 15 min, and finally permitted the steel to cool to room temperature. Did he produce the required bainitic structure? Use the diagram below in your answer 900 600 700 14 00 Y. 400 12 52 M. 00 57 M. 100 0.3 10 10 10 Answer: Time Temperature ("C) Rockwell Chardnens
For a 9 wt % Fe-l wt% C steel at a temperature 1600 1538°C Composition tat C) 10 15 20 25 just below the 1493 eutectoid, determine the 1400 'A 2500 following: 1394°C 1200- 1147°C a) The 2,14 7. Austenite 4.30 2000 compositions 1000- 912°C 1. FegC of Fe;C and ferrite (a). 800 1500 727°C O 76 D. 0.022 600 - a. Ferrite *• FezC Cementite (FezC) 1000 400 6. 6.70 3 (Fe) Camposition (w% C) b) The amount of cementite (in grams) that forms in 100 g of steel. c) Sketch the developed microstructure as it is cooled from liquid phase region to below the eutectoid temperature (at least 4-different regionsA, B,C,D), o.) anjeadua Termpar ature (F)
The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite; the mass fractions of these two microconstituents are 0.300 and 0.700, respectively. Determine the concentration of carbon in this alloy. The iron-iron carbide phase diagram is shown in the Animated Figure 9.24. i wt% C
The phase diagram of the alloy Copper – Silver is shown in the figure below. Composition (at% Ag) 20 100 2200 40 60 80 1200 2000 A -Liquidus 1000 Liquid 1800 -Solidus F a +L 779°C (Tg). 1600 B+L 9 800 E B G 91.2 (Cog 8.0 71.9 1400 1200 600 1000 Solvus a +B 800 400 C 600 H 200 0 60 400 100 20 40 80 (Cu) Composition (wt% Ag) (Ag) (a) Cite the phases that are present and the phase compositions for the following alloys: 1) 5 wt% Cu – 95 wt% Ag at 900 °C 2) 50 wt% Cu – 50 wt% Ag at 1000°C 3) 30 wt% Cu – 70 wt% Ag at 900 °C 4) 20 wt% Cu - 80 wt% Ag at 600 °C 5) 40 wt% Cu – 60 wt% Ag at 600 °C (b) Determine the eutectic temperature and eutectic composition. (c) What is the maximum solubility of silver in copper and at which temperature? Temperature ("C) Temperature ("F)
Q3: Analyze the following figure and answer the following question (Fe-C Diagram) ? 1639 Liquid 1400 +y 7+L L-Fec 1146 C Fe.C- 910 7- Fesc 727 C o.025 a- Fesc 6.67 of Hypo ectd- Hyper ectd 0810 Steel Cast Iron I- What are the % solubility and temperature of exist of a-ferrite? b- 0.025% and 273°c to 910 c. d- 0.05% and 910°c to 1124°c. a-0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. 2- What are the % solubility and temperature of exist of Austenite (Y)? a- 0.05% and 273°c to 910°c. c- 2.1% and 910°c to 1394°c. b- 0.025% and 273°c to 910°c. d- 0.09% and 1394°c to 1539°c. 3- What are the % solubility and temperature of exist of 8-ferrite? a- 0.05% and 273°c to 910°c. b-0.025% and 273 e to 910°e. c- 2.1% and 910°c to 1394°c. d- 0.09% and 1394°c to 1539°c. 4- What is the % C content in Cementite Fe3C? AB a- 6.67%. b- 0.025%. c- 2.1%. d- 0.09%. (aradu
Consider 0.60 kg of austenite containing 1.3 wt% C, cooled to below 727°C (1341°F). Using the iron-iron carbide phase diagram, Animated Figure 9.24, determine the following: (a) How many kilograms of total ferrite form i kg (b) How many kilograms of total cementite form i kg (c) How many kilograms of pearlite form kg (d) How many kilograms of the proeutectoid phase form i kg
Temperature (°C) 1600 1400 1200 1000 800 600 1538°C 400 0 912°C (Fe) + -1493°C 1394°C y, Austenite 0.76 0.022 a, Ferrite 5 y+L 2 2.14 Composition (at % C) 15 10 1147°C a + Fe3C L 4.30 y+ Fe3C 4 3 Composition (wt% C) 727°C 20 Cementite (Fe3C). 5 6 25 2500 2000 1500 1000 6.70 Temperature (°F)