Q2) Cylindrical rod with original diameter (12mm) and original length (70 mm) made of 1020 Hot-rolled steel alloy which their yield stress (207 MPa) and Young modulus (210 GPa). Tensile test was carried on this rod and it's broken under (27.5 KN) force with final diameter (10mm) and final length (84 mm). Calculate: (A) 1- Engineering fracture stress 2- True fracture stress. (B) If you know that the Brinell hardness for this alloy (HB=111). Estimate the tensile strength of this alloy in (MPa).

Q2) Cylindrical rod with original diameter (12mm) and original length (70 mm) made of 1020 Hot-rolled steel alloy which their yield stress (207 MPa) and Young modulus (210 GPa). Tensile test was carried on this rod and it's broken under (27.5 KN) force with final diameter (10mm) and final length (84 mm). Calculate: (A) 1- Engineering fracture stress 2- True fracture stress. (B) If you know that the Brinell hardness for this alloy (HB=111). Estimate the tensile strength of this alloy in (MPa).

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Example: Convert the change in length data in Table 3-2 to engineering stress and strain and plot a stress-strain curve Homework- help Table 3-2 The results of a tensile test of a 0.505 in. diameter aluminum alloy test bar, initial length (1o) = 2 in. Calculated LTO Load (Ib) Change in Length (in.) Stress (psi) Strain (in./in.) 0.000 1000 0.001 0.0005 4,993 14,978 24,963 34,948 37,445 39,442 39,941 39,691 37,944 3000 0.003 0.0015 5000 0.005 0.0025 7000 0.007 0.0035 7500 0.030 0.0150 7900 0.080 0.0400 8000 (maximum load) 0.120 0.0600 7950 0.160 0.0800 7600 (fracture) 0.205 0.1025
*O llAsiacell Strength of m. -> 02: A steel specimen 12mm diameter has gauge length 50mm. the steel specimen had tested via tensile test under maximum load 66KN with elongation 7.5mm, and the yield load of this specimen is 15KN with elongation 2.4mm. Calculate: 1- The engineering ultimate stress (ultimate tensile strength), and engineering strain at this point. 2- The engineering stress and strain at yield point. 3- The modulus of elasticity, and the modulus of resilience. 4- The final or fracture strain of a steel specimen, if you know that the final length of specimen after testing is 58.5mm. 5- The true stress and strain for ultimate point. Q3: The yoke-and-rod connection is subjected to a tensile force of 15 kN. Determine the average normal stress in each rod and the average shear stress in the pin A between the members. Finally, find the shear strain in pin A. Take G teef 75GPA 40 mm 15 kN, 30 mm 30 mn 15 kN 04: In figure as shown below, assume that a 35mm diameter rivet joint the…
A tensile test for a copper specimen has been performed and the following data are obtained. - Percentage of Elongation = 69 % - Percentage of Reduction in Area = 39 % - Final length after fracture = 35.5 mm - Final Diameter after fracture = 3.6 mm & - Ultimate stress = 396 MPa SOLUTION: iv) Initial Diameter (in mm) = v) Ultimate Load (in N) =
In the state of loading as made of brittle material tensile and compression fracture values of the exposed arm, respectively. σUT=200 MPa and σUC=800 MPa and factor of safety n=4 as it is; a) First reduce the applied forces to point B, b) By determining the critical point of the critical section and stresses Calculate it and show it on the stress element. c) Calculate the diameter of the AB part according to the Coulomb criterion. Note: Neglect the effect of cutting forces.
The Highest load sustained druing an uniaxial tensile testing experiment is 7,500lb. If the original cross section has a diamter of 0.25in, what is the ultimate tensile strength? (please also make a drawing)
The table below shows the deformation data that resulted from applying a pure tensile load to a brass alloy rod with an initial length of 30 mm and a diameter of 10 mm. This rod was subjected to necking and beyond necking deformation. The data at fracture is shown in the last row. Applied Load (N) Length (mm) Diameter (mm) 75,100 33.8 68, 250 34.9 50,200 35.7 6.7 Solve for the TRUE STRESS/ES and TRUE STRAINS. 8.3 7.8
a)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?
A tensile test was conducted on a mild steel& the following data was obtained as follows. Diameter of the steel bar = 3 cm,Gauge length of the bar = 20 cm. Load at elastic limit = 250 kN . Extension at a load of 150kN = 0.21 mm . Maximum load = 380 kN . Total extension = 60 mm . Diameter of the rod at failure = 2. 25 cm Determine: (a) Young’s modulus (b) stress at elastic limit (c)the percentage of elongation (d) Percentage decrease in area.
A stress-strain diagram for a tension test of an alloy steel sample is shown in the diagram below. The initial sample diameter is 0.502”, the diameter of the fractured sample is 0.412”, the original gage length is 2.00” and the final length after fracture is 2.78”. Determine/ calculate the following: (a) The stress at the proportional limit. (b) The modulus of elasticity (E). (c) The yield stress using the 0.2% offset method. (d) Theultimatetensilestrength. (e) The rupture stress. (f) The percent reduction in area. (g) The percent elongation. (h) Is the material considered ductile or brittle?
. From the tensile stress-strain behaviour for a casted iron as shown in the following curve. Please answer the following questions (1) Estimate the modulus of elasticity, (2) Calculate the change in length of a specimen with original length of 100mm that is subjected to a tensile stress of 300MPa. (Hint: Using the Hooke's law to get the strain.) 600 500 400 - 300 - 200 - 100 - 2 4 6. 8 10 12 14 16 Strain Strength (MPa)
1. A steel rod is subjected to tension force (diameter: 30 mm) is made of annealed AISI 1015 steel. Yield strength of the annealed AISI 1015 steel is 386 MPa. (a) If the test specimen yielded when it was subjected to tensile force P, calculate P. yielding if the applied tensile force P is 1,200 kN. (b) Calculate safety factor against 30mm
yields under a load of 8KN; it attains a max load of 15KN and breaks finally A tensile test is carried out on a bar of mild steel of diameter 20mm. The bar Еxample at a load of 7KN. Estimate yP (i) The tensile stress at the yield point (ii) The ultimate tensile test ii. Max loa (iii) The average stress at the breaking point if the diameter of neck is Omm.