The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 7.81 x 10-17 7.70× 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i T (°C) 1030 i 1260 J/mol m²/s (Use scientific notation.) (c) What is the magnitude of D at 1180°C? m²/s (Use scientific notation.)

The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 7.81 x 10-17 7.70× 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i T (°C) 1030 i 1260 J/mol m²/s (Use scientific notation.) (c) What is the magnitude of D at 1180°C? m²/s (Use scientific notation.)

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

The diffusion coefficients for species A in metal B are given at two temperatures: D (m²/s) 8.54 x 10-17 8.39× 10-16 i (b) Determine the value of Do. (a) Determine the value of the activation energy Qd (in J/mol). i J/mol i T (°C) (c) What is the magnitude of D at 1190°C? 1020 1290 m²/s (Use scientific notation.) m²/s (Use scientific notation.)
Using the Tabulation of Diffusion Data, answer the following: (a) Calculate the diffusion coefficient for Cu in Al at 520'C. 7.18e-14 m2/s (Use scientific notation.) (b) What time (in h) will be required at 620°C to produce the same diffusion result (in terms of concentration at a specific point) as for 12hat 520 C? i 2.52
Rank the magnitudes of the diffusion coefficients from greatest to least for the following systems: N in Fe at 700°C Cr in Fe at 700°C N in Fe at 900°C Cr in Fe at 900°C Now justify this ranking. (Note: Both Fe and Cr have the BCC crystal structure, and the atomic radii for Fe, Cr, and N are 0.124, 0.125, and 0.065 nm, respectively. You may also want to refer to Section 5.4.)
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values Diffusion coefficient D (cm²/s) ܐ ܐ ܐ ܐ 10- 10-5 10- 10-10 10-11 10-12 10-13 10-14 10-15 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 Cin graphite Mg in MgO Ca in Cao Hin FCC iron C in FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron C in BCC iron Fe in FeO 500 5 6 7 8 9 10 11 12 13 104 T(K) Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
Compare the diffusion coefficients (in cm²/s) of nitrogen in BCC and FCC iron at the allotropic transformation temperature of 912°C. Decc -153606 X Your response differs from the correct answer by more than 10%. Double check your calculations, cm²/s -1976-7 Dicc x Your response differs significantly from the correct answer. Rework your solution from the beginning and check each step carefully. cm2/s
What temperature is required to obtain 0.4%C at a distance of 0.3 mm beneath the surface of a 0.22% C steel in 2h, when 1.1% C is present at the surface? Assume that the iron is FCC. (Please see figure 5.12 below for diffusion coefficient data. Please use your notes for a table of erf() function values table of erf() fun Diffusion coefficient D (cm²/s) 10-3 !! ! ! ! ! 10- 10-5 10-9 10-10 10-11 10-12 10-13 10-14 Temperature (°C) 2000 1500 1200 1000 900 800 700 600 wwwwwwwwwwwwwww in graphite Mg in MgO Ca in CaO H in FCC iron Cin FCC iron Fe in FCC iron Fe in BCC iron H in BCC iron 104 T(K) C in BCC iron Fe in FeO 500 10-15 4 5 6 7 8 9 10 11 12 13 Figure 5-12 The diffusion coefficient D as a function of reciprocal temperature for some metals and ceramics. In this Arrhenius plot, D represents the rate of the diffusion process. A steep slope denotes a high activation energy.
Question 1Helium gas is contained in a cylinder by a gas-tight piston which can beassumed to move without friction. The gas occupies a volume of 1 x 10^-3m^3 temperature of 300K and a pressure of 1 x 10^5 Pa.(a) Calculate :i.the number of helium atoms in the container,ii.the total KE of the helium atoms(b) Energy is now supplied to the gas in such a way that the gas expands andthe temperature remains constant at 300K. State, and explain what changes, if any, will have occurred in the following quantities :i. The internal energy of the gasii. The root-mean-square speed of the helium atomsiii. The density of the gas.(Given : Boltzmann's constant = 1.38 x 10^23 JK^-1)
Diffusion of carbon into BCC iron for 12 hours at a temperature of 500 °C results in a carbon concentration of 0.2 wt% at a depth 2 mm from the surface. How long would it take to get a concentration of 0.2 wt% at a depth 3 mm from the surface at 500 °C?
Calculate the value of the diffusion coefficient D (in m2/s) at 750°C for the diffusion of some species in a metal; assume that the values of D0 and Qd are 5.6 × 10-5 m2/s and 177 kJ/mol, respectively.
In an electrochemical cell, a metal anode lost 0.227 g while a total volume of 0.08149 L of hydrogen gas was produced. The temperature was 298 K and the barometric pressure was 745.4 mm Hg. At 298 K, the vapor pressure of water is 23.8 mm Hg. How many moles of hydrogen gas were collected?
The diffusion coefficients for carbon in nickel are given at two temperatures: T("C) D(m2/s) 600 5.5 x 10-14 700 3.9 x 10-13 (a) Determine the value of Do. i m2/s (Use scientific notation.) (b) Determine the value of Qd. kJ/mol (c) What is the magnitude of D? at 860°C. i m2/s (Use scientific notation.)
5-15 Compare the diffusion coefficients of car- bon in BCC and FCC iron at the allotropic transformation temperature of 912°C and explain the difference.