Two polymer bars are connected to a rigid plate at 8, as shown. Bar (1) has a cross-sectional area of 1.42 in.and an elastic modulus of 2180 ksi. Bar (2) hasa cross-sactional area of 1139 in.and anelastic modulus of 4150 ksi. Assume l-23 in., L-41 in, Q-6.7 kips, P-3.7 kips, and R-14.1 kips. Datermine the horizontal deflection of end Crelative to end A P R (1) (2) Answer: uga in.

Two polymer bars are connected to a rigid plate at 8, as shown. Bar (1) has a cross-sectional area of 1.42 in.and an elastic modulus of 2180 ksi. Bar (2) hasa cross-sactional area of 1139 in.and anelastic modulus of 4150 ksi. Assume l-23 in., L-41 in, Q-6.7 kips, P-3.7 kips, and R-14.1 kips. Datermine the horizontal deflection of end Crelative to end A P R (1) (2) Answer: uga in.

Steel Design (Activate Learning with these NEW titles from Engineering!)

6th Edition

ISBN:9781337094740

Author:Segui, William T.

Publisher:Segui, William T.

Chapter1: Introduction

Section: Chapter Questions

Problem 1.5.6P: The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular...

See similar textbooks

Similar questions

The data in Table 1.5.3 were obtained from a tensile test of a metal specimen with a rectangular cross section of 0.2011in.2 in area and a gage length (the length over which the elongation is measured) of 2.000 inches. The specimen was not loaded to failure. a. Generate a table of stress and strain values. b. Plot these values and draw a best-fit line to obtain a stress-strain curve. c. Determine the modulus of elasticity from the slope of the linear portion of the curve. d. Estimate the value of the proportional limit. e. Use the 0.2 offset method to determine the yield stress.
X Your answer is incorrect. Two polymer bars are connected to a rigid plate at B, as shown. Bar (1) has a cross-sectional area of 1.42 in.? and an elastic modulus of 2180 ksi. Bar (2) has a cross-sectional area of 1.139 in.? and an elastic modulus of 4150 ksi. Assume L;-23 in., L2-41 in., Q-6.7 kips, P-3.7 kips, and R-14.1 kips. Determine the horizontal deflection of end Crelative to end A. R (1) (2) P L1 L2 Answer: UCIA - i 0.0725 in.
Two polymer bars are connected to a rigid plate at B, as shown. Bar (1) has a cross-sectional area of 1.58 in. and an elastic modulus of 2430 ksi. Bar (2) has a cross-sectional area of 0.714 in and an elastic modulus of 4110 ksi. Assume Ly-18 in., Lz-47in, Q=6,4 kips, P-3.2 kips, and R-128 kips. Determine the horizontal deflection of end Crelative to end A. (1) Answer: uCA in.
A steel bar with diameter d1 = 10 mm has upset ends with diameter d2 = 15 mm. The lengths of the bar segments are L1=0.3 m and L2=0.15 m. The radius at the transition R = 1.25 mm and the modulus of elasticity is 90 GPa, the bar product of the load p elongates 0.12 mm normal stress and maximum stress
The shown plate is 60 mm thick and it is made of Magnesium Am1004-T61. The plate is fitted between the rigid frictionless supports as shown and at T, = 20°C it is stress free. Find the stresses in the x and y directions when the temperature increases to T, = 58°C. %3D 150 mm 150 mm Select one: O x: 0 MPa, y: 42.864 MPa Ox: 22.1 MPa, y: 44.2 MPa Ox: 0 MPa, y: 44.2 MPa Ox: 0 MPa, y: 17.8 MPa O x: 13.2 MPa, y: 44.2 MPa Ox: 0 MPa, y: 67.4 MPa 3:10 PM O G 4) ENG 1/31/2021
An aluminum alloy [E = 73 GPa; v = 0.33; a= 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 250 mm, a cross-sectional area of A = 6900 mm², and a length of L = 5.9 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 50°C, the longitudinal normal strain in the plate is found to be 2400 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L Answer: (a) P = i (b) Δd = KN mm
SITUATION. As shown in the figure below, a rigid bar with negligible mass is pinned at O and attached to two vertical rods. Assume that the rods were initially stress-free. Allowable stress in steel is 120 MPa and in bronze is 60 MPa. For this problem, a = 1.8m; b = 1.3m; c = 1.7m. b C NANTSELEINE Steel: A = 900 mm² E = 200 GPa L=1.5m Bronze: A=1200 mm² E=83 GPa L=2.0m What is the ratio of the elongation of steel to bronze? O 0.367 O 0.433 O 0.467 0.333
A steel bar with diameter d1 = 10 mm has upset ends with diameter d2 = 15 mm. The lengths of the bar segments are L1=0.3 m and L2=0.15 m. The radius at the transition R = 1.25 mm and the modulus of elasticity is 90 GPa, the bar product of the load p elongates 0.12 mm maximum stress
An aluminum alloy [E = 74 GPa; v = 0.33; a = 23.0 x 10-6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 265 mm, a cross-sectional area of A = 5300 mm², and a length of L= 4.2 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by AT = 57°C, the longitudinal normal strain in the plate is found to be 2920 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Ad. L P Answer: (a) P = i (b) Δd = i kN mm
A bar obtained by bonding together pieces of steel (Es = 29 x 106 psi) and brass (E = 15 x 106 psi) has the cross section shown (Fig. a). Determine the maximum stress in the steel and in the brass when the bar is in pure bending with a bending moment M = 40 kip-in. 0.4 in. 3 in. Brass 0.75 in. Steel Brass 0.4 in. (a) 1) Composite bar.
An aluminum alloy [E = 67 GPa; ν = 0.33; α = 23.0 × 10–6/°C] plate is subjected to a tensile load P. The plate has a depth of d = 225 mm, a cross-sectional area of A = 5100 mm2, and a length of L = 4.1 m. The initial longitudinal normal strain in the plate is zero. After load P is applied and the temperature of the plate has been increased by ΔT = 63°C, the longitudinal normal strain in the plate is found to be 2900 με. Determine: (a) the magnitude of load P. (b) the change in plate depth Δd.
Problem 1.5-2 A bar of length 2.0 m is made of a structural stoel having the stres-strain dingram shown in the figure. The yield stresa of the steel is 250 MPa and the slope of the initial lincar part of the stress-strain curve (modulus of elasticity) is 200 GP. The bar is loaded axially until it eklongates 6.5 mm, and then the load is removod. How does the final length of the bar compare with its orig- inal length? Hint: Ue the concepts illustrated in Fig. 1-36h) MP 300 200 100 0.002 0.004 0.006