Answered: Hard soldering of metals can be done in…

Hard soldering of metals can be done in the melting point temperature range of O 183°C-212°C 650°C-700°C O 1600°C-1700°C O 6000°C-7000°C

Welding: Principles and Applications (MindTap Course List)

8th Edition

ISBN:9781305494695

Author:Larry Jeffus

Publisher:Larry Jeffus

Chapter26: Welding Metallurgy

Section: Chapter Questions

Problem 35R: Why must the stress-relieving temperature be kept be-low the critical temperature of the plate?

See similar textbooks

Related questions

Q: What does liquid-solid phase bonding mean and in which cases is it preferred over welding? What does…

A: The liquid-solid phase bonding is a joining technique that has been used to join a variety of…

Q: For a cross section of a typical fusion-welded joint: (a) list all types of different zones in the…

A: The microstructure and grain size of the welded joint depend on the amount of heat applied and the…

Q: (b) Two flat aluminum sheets (each 1 mm thick) are being spot welded by use of a current of 5000A…

Q: A resistance spot-welding operation is performed on two pieces of 1.5 mm thick sheet steel using…

Q: Solidification cracking in weldments occurs at 1) moderate temperature 2) very high temperature 3)…

A: Given :- Solidification cracking in weldments occurs at 1) moderate temperature 2) very high…

Q: What must be the thickness of a plate 350mm-wide to withstand a force of 250kN if the working stress…

A: Normal Stress = Force/ Area normal to the force. here, stress= 150 Mpa Force = 250 KN = 250000N Area…

Q: What is a cold solder joint? Identify its causes, its appearance, and the means of correction.

Q: An ECM operation is used to cut a square-shaped blind hole into a nickel block (valence = 2). The…

Q: accuracy of the finished workpiece in welding works? Is it possible to have an accurate workpiece…

A: INTRODUCTION Welding desertsWeld deformities, for example, breaking and porosity greatly affect the…

Q: 33- Which one of the followings is not used for heating the joining materials for soldering and…

Q: What are the parameters of inert gas welding process?

A: The parameters for the inert gas welding process are as follows: Welding Current Welding Voltage…

Q: what describe the soldering motheds in detail

Q: What is welding? What are the different types of welding? What are the symbols of welding?…

Q: Welding is a common method to join separate parts of metal together. Briefly describe the conditions…

A: Several industrial and production operations rely heavily on the welding process. Metals of all…

Q: What is metal inert gas welding and the effect of metal inert gas welding process parameters?…

A: what is metal inert gas welding?? answer-In this type of welding consumable type of electrode used.…

Q: 7) Which group of electrodes are best suitable for high temperatures during resistance spot welding?…

A: Solution:

Q: why Filler metals are used in fusion welding process?

A: Filler metal Filler metal is a metal added in the making of a joint through welding, brazing, or…

Q: Identify the conditions under which a brazed joint is likely to be “stronger” than the brazing…

A: Since you have asked multiple questions, we will solve the first question for you. If you want any…

Q: Why are rivets of a 2017 aluminum alloy often refrigerated until the time they are used?

A: Hardness and strength of some material can be improved by Precipitation Hardening. Precipitation…

Q: What are the advantages of MIG welding on stainless steels?

A: MIG : (Metal Inert Gas) It is a type of arc welding. MIG welding is carried out by placing an arc…

Q: The temperature range for soldering process is 1) 40°C to 100°C 2) 180°C to 250°c 3) 300°C to 500°C…

A: Soldering is a process of joining of metals with non ferrous filler metal. The temperature is below…

Q: What are the disadvantages of MIG welding on stainless steels?

A: Before answering above question, we should know the physical and chemical properties of stainless…

Q: Which of the following is not a factor that strengthened soft solder joints? a. Solder composition…

A: Soft soldering is a technique for connecting metals that uses a Eutectic Tin/Lead Alloy.…

Q: If you need narrow deep penetration weld for heavv base metal, which type of current polarity you…

A: Solution:

Q: Give detail classification of all welding processes and their practical applications

A: Classification of welding.

Q: 8) The correct ways to control liquation cracking tendency in fusion weld joint are I. Use of filler…

A: The way of arranging and control liquation cracking tendency in fusion is iii, iv and v

Q: Enumerate the different types of riveted joints and rivets.

A: Rivets and Riveted Joints

Q: Hard soldering uses alloy of silver and _______ metal. a. Zinc b. Tin c. Lead d. Copper

Q: Which of the following best explains why the exothermic nature of the reaction is important to the…

A: Here option (D), The reaction releases heat, which is then absorbed by the products, so they melt,…

Q: 5) Which one of the following options is true about friction stir welding? Fine microstructure is…

A: Solution:

Q: (a) Discuss the differences between fusion and solid state welding.

Q: Briefly explain the heat-affected zone (HAZ) in welding showing the microstructural changes with a…

Q: Describe at least five main functions carried out by coating on electrode in electric arc welding…

Q: (a) Describe brazing and soldering processes. (b) Two parts made of steel were joined by adhesive…

A: a) Brazing process it is process of metal-joining where two or more than two metals are joined…

Q: The temperature range of hard soldering process is __________________. a. 183-212 C. b. 650-700 C.…

A: Answer is (b) 650-700 C

Concept explainers

Joining Processes

It is the process of permanent or temporary joining of two metal pieces with the help of heat or pressure. Two metal parts are assembled by applying an energy source for the formation of a single unit. The obtained joined metals cannot be fragmented easily with the application of any force.

Question

Hard soldering of metals can be done in the
melting point temperature range of
O 183°C-212°C
650°C-700°C
O 1600°C-1700°C
O 6000°C-7000°C

Expert Solution

This question has been solved!

Explore an expertly crafted, step-by-step solution for a thorough understanding of key concepts.

This is a popular solution!

SEE SOLUTION Check out a sample Q&A here

Step 1

VIEW

Step 2

VIEW

Trending now

This is a popular solution!

Step by step

Solved in 2 steps

SEE SOLUTION Check out a sample Q&A here

Knowledge Booster

Learn more about

Need a deep-dive on the concept behind this application? Look no further. Learn more about this topic, mechanical-engineering and related others by exploring similar questions and additional content below.

Similar questions

Why must the stress-relieving temperature be kept be-low the critical temperature of the plate?
Why does the hardness decrease at 600 ° C after rising when the tempering process
4. As shown in Figure 13, the top cover of the quenching furnace is lifted by a single acting cylinder, the load on the piston rod is 9kg, the known stroke of the top cover is 250mm, the piston area is 2cm, and the flow rate of the pump is 3L/min. Please calculate the following values: load pressure, forward stroke speed and time. Figure 13
What are the disadvantages of MIG welding on stainless steels?
What are the advantages of MIG welding on stainless steels?
8) The correct ways to control liquation cracking tendency in fusion weld joint are I. Use of filler metal that solidifies before the partially melted zone I. Use of single pass welding with higher net heat input instead of multipass welding III. Use of high energy density processes IV. Preheating the substrates V. Use of base metals with fine grain structure OI, II, and III II, and IV OII, IV, and V O II, III and IV
What are the possible defects of MIG welding on stainless steels?
5) In soft soldering a low melting range alloy of tin and lead is used as filler metal. Select one: True False
36 Asiacell O Homework 4 -... -> 3 Class Materials Eng. Dep. Heat Treatment Ismail Ibrahim Marhoon Homework 4 Q1: 1.5 in diameter steel part is quenched in oil with no agitation. (H=0.20). If we use a 4340; 4140; 8640; 5140; 1040 steel, what would be the hardness number at the center of the part? Q2: Determine the best quenching medium to produce a minimum hardness of HRC 40 at the center of a 3.75 cm diameter 4320 steel bar. Given Cingrate t 00c00 143 to 4340 50 40 8640 ab 9310 30 4320 1050 1040 10 20 it 1 1 2n 10 20 30 Jominy distance th of an inch) Die he eted e TABLE The N canticient, or seveity of the querch, far several guenehing sedla H Coefticient Coaling Rate at he Center of a l-in. Bar (CA) Medium Ol no taton) 04 anitation) 025 18 45 HyD inc agtation H0 fegiutont Brine Ino agtaton) Brine lapttiori 10 4.0 190 20 60 90 230 Ad DISTANCE FROM OUENCHED END IN) DIAMETER IN)
How would you use the principle measure the heat output of something? For design a setup that can be used to measure the heat output of an ironing press.
Using Castigliano’s Theorem
Welding stainless steel is a complicated process because (uniform / intergranular / erosion) corrosion may happen, to avoid this issue post-weld-heat treatment is conducted to (precipitate / dissolve) carbide particles.